Issues on 10.1016/j.ceramint.2024.11.089

Parts (in purple boxes) of the lines in Figure 2, the noise patterns look too similar to each other than expected. And the XRD patterns presented in Figure 2 are not consistent to those presented in Figure 4.

Title: Effects of La3+ doping on the structural, vibrational, elemental, and dielectric characteristics of Sr-Ba-Zr2 R-type hexaferrite

Authors: Iqra Manzoor (The Islamia University of Bahawalpur, Pakistan), M. Irfan (The Islamia University of Bahawalpur, Pakistan), Raqiqa Tur Rasool (Zhejiang Normal University/浙江师范大学, China), Majid Niaz Akhtar (The Islamia University of Bahawalpur, Pakistan), Muhammad Khalid (GC University Faisalabad, Pakistan), Abdullah Almohammedi (Islamic University of Madinah, Saudi Arabia), Mustafa Mahmoud (King Khalid University, Saudi Arabia), Muhammad Aslam (Ural Federal University, Russia, and Middle East University, Jordan), Tahir Ali Sheikh (The Islamia University of Bahawalpur, Pakistan), Ghulam Abbas Ashraf (New Uzbekistan University, Uzbekistan), Muhammad Azhar Khan (The Islamia University of Bahawalpur, Pakistan)

Journal: Ceramics International

Publication Year: 2025

Funding: Deanship of Research and Graduate Studies at King Khalid University for funding this work through Large Research Project under grant number RGP2/433/45








Author: WU Guangheng

Founder and Chair of the 5GH Foundation

E-Mail: wu@5gh.org.cn

Document ID: 5GH-WuGH-2025.000073

Publication Date: 2025.07.06

This article is licensed under a CC BY-NC-ND 4.0 International License

Issues on 10.1016/j.materresbull.2024.112716

The black and pink lines in the Figure 2 are identical to each other. The red and green lines in the Figure 2 are identical to each other. An erased sub-figure is also observed in Figure 2.


Issues on 10.1016/j.ceramint.2021.03.291

In the pink line of Figure 1, parts highlighted by same colour boxes look identical to each other, suggesting this line was manipulated.


Abnormal Background of EDX and Other Issues on 10.3390/applnano4030013